Different mass ratio proportions of PtSn (m/m) electrocatalysts with 20% metal loading on a carbon support were prepared for use in ethanol:methanol solutions oxidation reactions. PtSn/C (3:1) (91% alloy degree, lattice parameter of 0.399 nm and mean crystallite size 4.8 nm) presented the best activity for oxidation of mixed solutions. The highest normalized current (ethanol:methanol 80:20) was 4.2 mA mgPt-1 (measured after 1800 seconds at 0.5 V). Therefore, the PtSn/C (3:1) electrocatalyst with an atomic ratio of 65:35 enhanced both the electronic effect and bifunctional mechanism in (ethanol:methanol 80:20), which resulted in the formation of CO2 at low potentials, as well as the highest amount of by-products than ethanol and methanol.

A deposição em subtensão de Cd sobre Pt e Au policristalinos foi estudada por voltametria nos eletrodos estacionário e de disco-anel rotatório. Sobre Pt, os picos de redissolução do Cd ads se sobrepõem àqueles relacionados com a oxidação do Hads, dificultando assim a avaliação precisa das cargas de dessorção. Um modelo proposto para se calcular estas cargas a partir de voltametria no eletrodo estacionário revelou um valor de 285 miC cm-2 para a monocamada completa, o que corresponde a um recobrimento de 90%, com os ad-átomos de Cd apresentando uma valência de eletrossorção de 0,5. Os resultados obtidos com a técnica de coleção do eletrodo rotatório confirmam plenamente estes valores. A diferença entre os tamanhos dos raios atômicos do Cd e da Pt justificam o recobrimento de menos de 100%. Por outro lado, sobre Au, a ausência de Hads simplifica o procedimento para a determinação das cargas de redissolução da monocamada de Cd. Aqui, um valor de apenas 41 miC cm-2 foi calculado, o que corresponde a um recobrimento máximo de 15%, com valência de eletrossorção de 0,5. Os resultados obtidos com os experimentos de coleção estão em perfeita concordância com estes valores.

The underpotential deposition of Cd on polycrystalline Pt and Au was studied by voltammetry at stationary and rotating ring-disc electrodes. On Pt, the Cd ads dissolution peaks overlap those related to the oxidation of Hads, thus hindering the precise evaluation of desorption charges. A model proposed to calculate such charges from voltammetry at stationary electrodes revealed a value of 285 muC cm-2 for the monolayer dissolution, which corresponds to a coverage of 90% with Cd ads presenting an electrosorption valence of 0.5. Rotating ring-disc experiments fully confirmed such values. The misfit between atomic radii of Cd and Pt justifies the less-than-100% coverage. On the other hand, on Au, the absence of Hads simplifies the procedure for determination of dissolution charges for the Cd monolayer. Here, a value of only 41 muC cm-2 was calculated, which corresponds to a maximum coverage of 15%, with the electrosorption valence of 0.5. The results obtained in the collecting experiments with the rotating electrode are in complete agreement with those values.